BI POWER

Its epoxy-polyurethane formulation makes it ideal for high-frequency use environments and for professionals seeking high performance, reliability and manageable processing times.Key Features

• Two-component paste adhesive (A + B)
• Ideal for any type of parquet: lamparquet, planks, multilayer, etc.
• High adhesion (>3 N/mm² on concrete and ceramics)
• Excellent strength and tightness even on non-absorbent substrates
• High flexibility and durability
• Low VOC emission (complies with indoor requirements)
• Predosed A:B ratio (9:1 by weight)

Dough preparation

• Component B is already included inside the container of component A.
• Pour the comp. B (1 part) at comp. A (9 parts) .
• Mix with mechanical stirrer at low speed until smooth.
  • In winter, mix only component A first to facilitate amalgamation.
• Usage time of the mixed product (pot life): 60-70 minutes

Application

• Apply with a notched trowel to a clean, dry and mechanically resistant substrate.
• The open time is about 1 hour at 23°C.
• Lay the parquet by applying even pressure.
• Always leave a perimeter joint of about 1 cm.
• Do not glue sideways and avoid filling the joints in prefinished.

• Walkability: after about 24 hours
• Smoothness: after 3 days (optimal: 7-10 days for maximum stability)

• Format: 10 kg predosed unit
  • Component A: 9 kg
  • Component B: 1 kg
• Consumption: 1000-1300 g/m² (notched trowel for parquet)
• Slurry color: uniform beige
• pH: not applicable – reaction adhesive
• Shore A hardness: 88 (after 7 days)
• Application temperature: +10°C to +30°C
• Operating temperature: -30°C to +70°C
• Shelf life: 24 months (in original sealed package, dry place)

• Component A: flammable and irritant
• Component B: corrosive

Both components may cause skin sensitization.
🔒 Use by professionals only.
🧤 Use gloves, protective goggles and work clothing during use.
📄 Always consult the updated MSDS.